This glass mostly used for Solar market and available with thickness of 3,2 mm and 4 mm
Patterned rolled sheet glass is colorless, having a different relief surface on both sides of the glass, which makes it possible to increase the transmittance of solar energy.
It is used in the manufacture of various modifications of solar modules and thermal collectors (solar systems) as a transparent insulation from the effects of external natural factors during operation.
It is produced in accordance with the requirements of European regulatory documents EN 572:2004, EN 12150, specifications of leading manufacturers of solar modules and collectors in Germany.
It is made using raw materials containing a minimal amount of iron, using a high-quality refractory stock at the glass ribbon forming section. The formation of glass tape on a rolling machine KVM6-2300 of the company "Flickert + Winterling" allows us to produce products of the required thickness with deviations of +/- 0.2 mm
characteristics for
Mat/Prismatic
Colorless
You can get additional information from our manager
| Glass is produced from sodium-calcium silicate raw material with the content of iron,% |
< 0,012 |
| The minimum value of the coefficient of directional light transmission at a glass thickness of 4.0 mm (the value of the index as per ND -0.82) |
0,91 (при содержании железа 0,012%) |
| The value of the total transmission of scattered light depending upon the pattern at a glass thickness of 4 mm (the value of the index as per ND is not less than 0.75) |
|
> 0,91 |
| The value of the residual internal stresses of glass (the value of the index as per ND - is not more than 100 nm/cm,) nm/cm |
up to 25 |
| Maximal glass sheet size |
3400х2300 |
| Available thickness |
3,2 and 4 mm |